Preparation, characterization, and applications of electrospun ultrafine fibrous PTFE porous membranes
来源:黄岩讲师个人网站 发布日期:2021-08-20
作者:Yan Huang;Qinglin Huang;Huan Liu; Chaoxin Zhang;Yanwei You; Nana Li;Changfa Xiao
关键字:Poly(tetrafluoroethylene) (PTFE);Electrospinning;Ultrafine fiber;Super-hydrophobicity;Membrane distillation (MD)
论文来源:期刊
发表时间:2017年
Ultrafine fibrous poly(tetrafluoroethylene) (PTFE) porous membranes (UFPPMs) were prepared by sintering electrospun PTFE/poly(vinylalcohol) (PVA) composite membranes. Meanwhile, poly(acrylonitrile) (PAN) nanofibers were co-electrospun to reinforcing the material. The effects of changing the PTFE/PVA mass ratio, the sintering temperature and the heating rate on the structure and properties of the resulting membranes were investigated. To observe the structure evolution of the ultrafine fibers during the sintering process, the prepared UFPPMs were characterized by scanning electron microscopy (SEM), atomic force microscopy (AFM) and static water contact angles (WCA). A unique interconnected fibrous network structure was formed. The spinning and sintering conditions were optimized. Moreover, the UFPPMs exhibited a super-hydrophobicity and an excellent lipophilicity. They also performed well in harsh water (saline feed solution 3.5 wt% NaCl and 10 wt% NaOH) membrane distillation experiments. The permeate flux stabilized at 14.53 L m?2 h?1 and the salt rejection remained above 99.8% after operating for 35 h.
Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号